Each Char. | Resin Grades | E0H | E3H | E120V | Ref. Resin | Ref. (Conditions Measurement) |
|
OH's Number | 00 | 03 | 120 | HIPS | ABS | ||
Mechanical Properties |
Tensile Strength (kgf/cm2) |
550 | 560 | 670 | 250 | 450 | JIS K7113 |
Tensile Modulus (kgf/cm2) |
1800 | 1800 | 1600 | 19000 | - | JIS K7113 | |
Tensile Elongation (%) | 4.0 | 4.0 | 4.0 | - | - | JIS K7113 | |
Flexural Strength (kgf/cm2) | 760 | 760 | 770 | 460 | 690 | JIS K7171 | |
Flexural Modulus (kgf/cm2) | 15000 | 16000 | 15000 | 21000 | 24000 | JIS K7171 | |
Bending Flexure Rate (%) | 14 | 13 | 14 | - | - | JIS K7171 | |
Compressive Strength (kgf/cm2) | 580 | 620 | 960 | - | - | JIS K7208 | |
Compressive Rate (%) | 4.0 | 4.0 | 17.0 | - | - | JIS K7208 | |
IZOD Impact Strength(kgcm/cm) | 2.0 | 2.5 | 2.0 | 9.0 | 16.0 | JIS K7110 | |
Heat and Electrical Properties |
Thermal Degradation Temperature (℃) | 420 | 423 | - | - | - | Temp. Programmed Speed in Nitrogen : 20℃/min |
Heat Distortion Temperature (℃) | 72 | 72 | 80 | 80 | 92 | JIS K7207, Load: 18.5kgf/cm2 | |
Combustion Quality(UL94) | - | HB | V-2 | HB | HB | 1/16" | |
Arc-Resistance(sec.) | 83 | 91 | - | - | - | ASTM D495 | |
Tracking Resistance | 250 | 275 | - | - | - | ICE 122 | |
Volume Resistivity (MΩ.cm) |
5.1×109 | 6.2×1010 | - | - | - | JIS K6911 | |
Physical Charac. |
Density (g/cm3) | 1.33~1.46 | 1.33~1.46 | 1.33~1.46 | 1.05 | 1.05 | |
Intrinsic Viscosity (dl/g) | 0.40 | 0.60 | - | - | - | At 25℃ | |
Melt Flow Rate (g/10min) | 40 | 30 | 45 | 7 | 17 | At : 265℃,ツꀀ Load : 1.05kg |
|
Others |
Characteristics |
PET Bottle Si |
Popular | Middle Impact resistance Flammability Not clear |
Popular | Popular |
Cautions: These physical properties are representation and are not guaranteed. Please reappraise according to each purpose in use. Moreover, the physical-properties value of reference resin was measured with method prepared for ASTM.